| 吸水率 | 0.02 | % | ASTM D-570 |
| 成形收縮率 | 東麗法 | ||
| 0.15 | % | ||
| 0.55 | % | ||
| 流動長 (320℃,98MPa,1mm厚) | 90 | ×10-3m | 東麗法 |
| 比重 | 1.96 | ASTM D-792 |
| 摩擦系數(shù) (對鋼) | 0.30 | ASTM D-1894 | |
| 拉伸強度 | 1.2 | % | ASTM D-638 |
| 硬度 | 123 | 洛氏 | ASTM D-785 |
| 彎曲彈性體 | 17.6 | GPa | ASTM D-790 |
| 彎曲強度 | 200 | MPa | ASTM D-790 |
| 斷裂強度 | 60 | ASTM D-732 | |
| 限界PV值 | 815 | kj/m.hr | 東麗法 |
| 沖擊強度 | ASTM D-256 | ||
| 90 | J/m | ||
| 20 | kj/m | ||
| 摩耗 | 70 | mg/1000回 | ASTM D-1044 |
| 引張強度 | 140 | MPa | ASTM D-638 |
| 耐電弧性W電級 | 182 | 秒 | ASTM D-495 |
| 誘電正接 (10Hz) | 0.002 | ASTM D-150 | |
| 誘電率 (10Hz) | 5.8 | ASTM D-150 | |
| 絕緣破壞電壓 | 15 | MV/m | ASTM D-149 |
| 體積固有抵抗 | 10 | Ω.m | ASTM D-257 |
| 熱變形溫度 (1.82MPa) | >260 | ℃ | ASTM D-648 |
| 線膨張系數(shù) | ASTM D-696 | ||
| 1.6 | ×10-5/K | ||
| 2.4 | ×10-5/K | ||
| 融點 | 278 | ℃ | DSC |
| 燃燒性 | V-0 | UL-94 |