| 吸水率 | 0.02 | % | ASTM D-570 |
| 流動長 (320℃,98MPa,1mm厚) | 100 | ×10-3m | 東麗法 |
| 比重 | 1.67 | ASTM D-792 | |
| 成形收縮率 | 東麗法 | ||
| 0.20 | % | ||
| 0.70 | % |
| 彎曲強度 | 270 | MPa | ASTM D-790 |
| 拉伸強度 | 2.3 | % | ASTM D-638 |
| 彎曲彈性體 | 12.7 | GPa | ASTM D-790 |
| 摩擦系數(shù) (對鋼) | 0.24 | ASTM D-1894 | |
| 引張強度 | 195 | MPa | ASTM D-638 |
| 絕緣破壞電壓 | 19 | MV/m | ASTM D-149 |
| 斷裂強度 | 80 | ASTM D-732 | |
| 限界PV值 | 900 | kj/m.hr | 東麗法 |
| 硬度 | 122 | 洛氏 | ASTM D-785 |
| 80 | ASTM D-256 | ||
| 120 | J/m | ||
| 65 | kj/m | ||
| 摩耗 | 55 | mg/1000回 | ASTM D-1044 |
| 耐電弧性W電級 | 123 | 秒 | ASTM D-495 |
| 體積固有抵抗 | 10 | Ω.m | ASTM D-257 |
| 誘電正接 (10Hz) | 0.002 | ASTM D-150 | |
| 誘電率 (10Hz) | 3.8 | ASTM D-150 |
| 線膨張系數(shù) | ASTM D-696 | ||
| 2.3 | ×10-5/K | ||
| 3.2 | ×10-5/K | ||
| 融點 | 278 | ℃ | DSC |
| 燃燒性 | V-0 | UL-94 | |
| 熱變形溫度 (1.82MPa) | >260 | ℃ | ASTM D-648 |