| 熔體流動(dòng)速率 (220℃/10kg) | 20 | g/10min | ASTM D-1238 |
| 比重 | 1.02 | ASTM D-792 | |
| 模具收縮率 | 0.4-0.7 | % | ASTM D-955 |
| 拉伸屈服強(qiáng)度 (50mm/min) | 380 | Kg/cm | ASTM D-638 |
| 拉伸模量 (1mm/min) | 16000 | Kg/cm | ASTM D-638 |
| 斷裂伸長(zhǎng)率 (50mm/min) | 40 | % | ASTM D-638 |
| 彎曲強(qiáng)度 (15mm/min) | 600 | Kg/cm | ASTM D-790 |
| 彎曲模量 (15mm/min) | 19000 | Kg/cm | ASTM D-790 |
| IZOD缺口沖擊強(qiáng)度 | ASTM D-256 | ||
| (1/4",23℃) | 40 | kg.cm/cm | |
| (1/4",-30℃) | 28 | kg.cm/cm | |
| (1/8".23℃) | 45 | kg.cm/cm | |
| (1/8".-30℃) | 33 | kg.cm/cm | |
| 洛氏硬度 | 90 | R-Scale | ASTM D-785 |
| 熱變形溫度 | ASTM D-648 | ||
| (未退火.18.5kg/cm,1/4") | 84 | ℃ | |
| (未退火.4.6kg/cm,1/4") | 88 | ℃ | |
| 維卡軟化點(diǎn) (5kg.50℃) | 93 | ℃ |