| 特性 | 阻燃性 |
| 用途 | 電氣/電子應(yīng)用領(lǐng)域 |
| 加工方法 | 注射成型 |
| 比重 | 1.18 | g/cm3 | ASTM D792 |
| 熔流率（熔體流動速率）(220°C/10.0 kg) | 60 | g/10 min | ASTM D1238 |
| 收縮率 - 流動(3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
| 洛氏硬度(R級) | 104 | ASTM D785 |
| 拉伸模量1(3.20 mm) | 2160 | MPa | ASTM D638 |
| 抗張強度2(屈服, 3.20 mm) | 43.1 | MPa | ASTM D638 |
| 伸長率3 | ASTM D638 | ||
| 屈服, 3.20 mm | 5.0 | % | ASTM D638 |
| 斷裂, 3.20 mm | 20 | % | ASTM D638 |
| 彎曲模量4(6.40 mm) | 2450 | MPa | ASTM D790 |
| 彎曲強度5(屈服, 6.40 mm) | 67.7 | MPa | ASTM D790 |
| 懸壁梁缺口沖擊強度 | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 78 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 260 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 240 | J/m | ASTM D256 |
| 載荷下熱變形溫度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40mm6 | 84.0 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 6.40mm7 | 76.0 | °C | ASTM D648 |
| 維卡軟化溫度 | 84.0 | °C | ASTM D15258 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 70.0 | °C | UL 746 |
| RTI | 75.0 | °C | UL 746 |
| UL 阻燃等級 | UL 94 | ||
| 1.00 mm | V-2 | UL 94 | |
| 2.10 mm | V-0 5VB | UL 94 | |
| 2.50 mm | V-0 5VA | UL 94 | |
| 3.00 mm | V-0 5VA | UL 94 |
| 干燥溫度 | 70.0 到 80.0 | °C | |
| 干燥時間 | 2.0 到 4.0 | hr | |
| 建議的大水分含量 | < 0.010 | % | |
| 料筒后部溫度 | 170 到 190 | °C | |
| 料筒中部溫度 | 180 到 200 | °C | |
| 料筒前部溫度 | 190 到 210 | °C | |
| 射嘴溫度 | 200 到 230 | °C | |
| 加工（熔體）溫度 | 200 到 230 | °C | |
| 模具溫度 | 40.0 到 60.0 | °C | |
| 背壓 | 0.490 到 0.981 | MPa | |
| 螺桿轉(zhuǎn)速 | 30 到 60 | rpm |
上海韜盛塑化科技有限公司 對比點擊按鈕將公司加入對比列表，詳細(xì)對比不同公司差異上海韜盛塑化科技有限公司是一家集貿(mào)易與生產(chǎn)研發(fā)為一體的商貿(mào)公司，代理經(jīng)營各國各種型號塑膠原料，以及生產(chǎn)各種改性工程塑膠.本公司主更多上海韜盛塑化科技有限公司是一家集貿(mào)易與生產(chǎn)研發(fā)為一體的商貿(mào)公司，代理經(jīng)營各國各種型號塑膠原料，以及生產(chǎn)各種改性工程塑膠.本公司主要研發(fā)生產(chǎn):ABS、POM、PC、HIPSPMMA、PC/ABS、PA66、PPO、PBT、K膠.....特種工程料：PPS、LCP、PEI、TPX、PA9T、PA6T、PA12、PA46、PTFE、PCTG、TPEE、PEEK、PC/PBT...增強系列：PP、PPS、PPO、PBT、PA、ABS、POM工程系列：PPS、LCP、PTFE、PEI、PPO、PBT、PEEK、PA6T、9T、PA46通用系列：ABS、PC、POM、PMMA、PA66、EVA、PC/ABS、HIPS、GPPS、PP、PVC以上僅為我公司部分供貨目錄。如有需要，歡迎來電來函洽談。