| 特性 | Good Heat Resistance 阻燃性 |
| 用途 | 電氣元件 電視外殼 |
| RoHS 合規(guī)性 | RoHS 合規(guī) |
| 加工方法 | 注射成型 |
| 比重 | 1.19 | g/cm3 | ASTM D792 |
| 熔流率（熔體流動(dòng)速率）(220°C/10.0 kg) | 30 | g/10 min | ASTM D1238 |
| 收縮率 - 流動(dòng)(3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
| 洛氏硬度(R級(jí)) | 108 | ASTM D785 |
| 拉伸模量1(3.20 mm) | 2060 | MPa | ASTM D638 |
| 抗張強(qiáng)度2(屈服, 3.20 mm) | 44.1 | MPa | ASTM D638 |
| 伸長(zhǎng)率3 | ASTM D638 | ||
| 屈服, 3.20 mm | 5.0 | % | ASTM D638 |
| 斷裂, 3.20 mm | > 20 | % | ASTM D638 |
| 彎曲模量4(6.40 mm) | 2550 | MPa | ASTM D790 |
| 彎曲強(qiáng)度5(6.40 mm) | 73.5 | MPa | ASTM D790 |
| 懸壁梁缺口沖擊強(qiáng)度 | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 59 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 240 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 180 | J/m | ASTM D256 |
| 載荷下熱變形溫度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 86.0 | °C | ASTM D648 |
| 維卡軟化溫度 | 93.0 | °C | ASTM D15256 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| UL 阻燃等級(jí) | UL 94 | ||
| 1.8 mm | V-1 | UL 94 | |
| 2.0 mm | V-0 5VB | UL 94 | |
| 3.0 mm | V-0 5VA | UL 94 |
| 干燥溫度 | 80 到 90 | °C | |
| 干燥時(shí)間 | 3.0 到 4.0 | hr | |
| 料筒后部溫度 | 170 到 190 | °C | |
| 料筒中部溫度 | 180 到 200 | °C | |
| 料筒前部溫度 | 190 到 210 | °C | |
| 射嘴溫度 | 200 到 230 | °C | |
| 加工（熔體）溫度 | 200 到 230 | °C | |
| 模具溫度 | 40 到 60 | °C | |
| 背壓 | 0.490 到 0.981 | MPa | |
| 螺桿轉(zhuǎn)速 | 30 到 60 | rpm |