| 流動(dòng)系數(shù) (200℃, 5kg) | 2.8 | g/10min | ASTM D-1238 |
| 比重 (23℃) | 1.19 | ASTM D-792 |
| 引張強(qiáng)度 | ASTM D-638 | ||
| (1/8",6mm/min) | 395 | kg/cm | |
| (1/8",6mm/min) | 5600 | lb/in | |
| 延伸率 (1/8",6mm/min) | 30 | % | ASTM D-638 |
| 彎曲強(qiáng)度 | ASTM D-790 | ||
| (1/4",2.8mm/min) | 620 | kg/cm | |
| (1/4",2.8mm/min) | 8800 | lb/in | |
| 彎曲彈性率 | ASTM D-790 | ||
| (1/4",2.8mm/min) | 25000 | kg/cm | |
| (1/4",2.8mm/min) | 350000 | lb/in | |
| IZOD缺口沖擊強(qiáng)度 | ASTM D-256 | ||
| (1/4",23℃) | 20 | kg-cm/cm | |
| (1/4",23℃) | 3.7 | ft-lb/in | |
| (1/8",23℃) | 24 | kg-cm/cm | |
| (1/8",23℃) | 4.4 | ft-lb/in | |
| 硬度 (1/2") | 98 | R Scale | ASTM D-785 |
| 維卡軟化點(diǎn) | ASTM D-1525 | ||
| (1/8",50℃/hr) | 104 | ℃ | |
| (1/8",50℃/hr) | 104 | ℉ | |
| 熱變形溫度 | ASTM D-648 | ||
| (85℃.8hr ,1/4",120℃/hr) | 96(85) | ℃ | |
| (85℃.8hr ,1/4",120℃/hr) | 205(185) | ℉ | |
| 燃燒率 | UL 94 | ||
| (1.6mm) | V-0 | ||
| (2.5mm) | 5VB |