| 熔體流動速率 | ASTM D-1238(ISO 1133) | ||
| (220℃×10kgf(98N)) | 20 | g/10min | |
| (200℃×5kgf(49N)) | 1.8 | g/10min |
| 比重 (23℃/23℃) | 1.05 | ASTM D-792(ISO 1183) |
| 洛式硬度 (23℃) | R-110 | ASTM D-785(ISO 2039/2) | |
| 拉伸強度 (23℃) | 530(52) | kg/cm(MPa) | ASTM D-638(ISO 527) |
| IZOD沖擊強度 (23℃) | 14(137) | kg.cm/cm(J/m) | ASTM D-256(ISO R180) |
| 彎曲強度 (23℃) | 870(86) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| 彎曲模數(shù) (23℃) | 28000(2750) | kg/cm(MPa) | ASTM D-790(ISO 178) |
| 維卡軟化點 (1Kg load) | 103 | ℃ | ASTM D-1525(ISO 306) |
| 燃燒性 (FILE NO E162823) | 1/16"HB All Color | UL 94 | |
| 熱變形溫度 | ASTM D-648(ISO 75/A) | ||
| (Unannealed 18.6kg/cm (1/2"厚)) | 88 | ℃ | |
| (Annealed (8℃×8hr)) | 100 | ℃ |