| 熔體流動(dòng)速率 (200℃.5kg) | 2.7 | g/10min | ASTM D-1238 |
| 比重 (23℃) | 1.03 | ASTM D-792 |
| IZOD缺口沖擊強(qiáng)度 | |||
| (1/4".23℃) | 16(3.0) | kg-cm/cm(ft-lb/in) | ASTM D-256 |
| (1/8".23℃) | 18(3.3) | kg-cm/cm(ft-lb/in) | ASTM D-256 |
| 引張強(qiáng)度 (1/8".6mm/min) | 450(6380) | Kg/cm(lb/in) | ASTM D-638 |
| 延伸率 (1/8".6mm/min) | 20 | % | ASTM D-638 |
| 彎曲彈性率 (1/4".2.8mm/min) | 24000(340000) | Kg/cm | ASTM D-790 |
| 彎曲強(qiáng)度 (1/4".2.8mm/min) | 680(9650) | Kg/cm(lb/in) | ASTM D-790 |
| 洛氏硬度 (1/2") | 110 | R Scale | ASTM D-785 |
| 軟化點(diǎn) (1/8".50℃/hr) | 104(219) | ℃(℉) | ASTM D-1525 |
| 熱變形溫度 (1/4".50℃/hr) | 98(209) | ℃(℉) | ASTM D-648 |
| 燃燒率 (1/16") | HB | UL 94 |