產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | 230℃/3.8kg | ASTM D-1238 | 5.6 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.05 | g/cm3 | |
| 模具收縮率 | Flow,3.20mm | ASTM D-955 | 0.50-0.80 | % | |
| 機(jī)械性能 | 拉伸模量 | ASTM D-638 | 2280 | MPa | |
| 拉伸屈服強(qiáng)度 | ASTM D-638 | 44.1 | MPa | ||
| 拉伸斷裂強(qiáng)度 | ASTM D-638 | 33.8 | MPa | ||
| 拉伸屈服伸長(zhǎng)率 | ASTM D-638 | 2.0 | % | ||
| 拉伸斷裂伸長(zhǎng)率 | ASTM D-638 | 24 | % | ||
| 彎曲模量 | 50.0mm Span | ASTM D-790 | 2340 | MPa | |
| 彎曲屈服強(qiáng)度 | 50.0mm Span | ASTM D-790 | 72.4 | MPa | |
| IZOD缺口沖擊強(qiáng)度 | 23℃ | ASTM D-256 | 320 | J/m | |
| IZOD缺口沖擊強(qiáng)度 | -30℃ | ASTM D-256 | 133 | J/m | |
| 熱性能 | 熱變形溫度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 96.0 | ℃ |
| 熱變形溫度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 80.0 | ℃ | |
| 維卡軟化溫度 | ASTM D-1525 | 98.0 | ℃ | ||
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000088 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000088 | cm/cm/℃ | |