| 比重 | 1.13 | ASTM D792 | |
| 成型收縮率 | 0.5-0.8 | % | ASTM D955 |
| 拉伸強度 | ASTM D638 | ||
| 560 | kg/cm | ||
| 55 | MPa | ||
| 7960 | psi | ||
| 斷裂伸長率 | ＞100 | % | ASTM D638 |
| 彎曲強度 | ASTM D790 | ||
| 790 | kg/cm | ||
| 77 | MPa | ||
| 11200 | psi | ||
| 彎曲模量 | ASTM D790 | ||
| 22500 | kg/cm | ||
| 2205 | MPa | ||
| 320 | psi | ||
| Izod缺口沖擊強度 | ASTM D256 | ||
| 65 | Kg.cm/cm | ||
| 635 | J/m | ||
| 12.0 | ft.ib/in | ||
| 洛氏硬度 | 110 | R | ASTM D785 |
| 熔融指數(shù) | 4 | g/10min | |
| 熱變形溫度 | ASTM D648 | ||
| (1.82MPa) | 108 | ℃ | |
| (1.82MPa) | 225 | ℉ |