| 模具收縮率 (3.2mm) | 4-6 | E-3 | ASTM D-955 |
| 吸水率 | 0.1 | % | ASTM D-570 |
| 比重 | 1.18 | ASTM D-792 |
| 洛氏硬度 | 121 | R | ASTM D-785 |
| 拉伸強(qiáng)度(屈伏點(diǎn)) | 64 | Mpa | ASTM D-638 |
| 拉伸模量 | - | Mpa | ASTM D-638 |
| 彎曲強(qiáng)度 | 96 | Mpa | ASTM D-790 |
| 沖擊強(qiáng)度缺口 (23℃) | 453 | J/m | ASTM D-256 |
| 彎曲模量 | 2584 | Mpa | ASTM D-790 |
| 拉伸率(斷裂點(diǎn)) | 40 | % | ASTM D-638 |
| 體積電阻 | 2.0E+17 | Ohm-cm | ASTM D-257 |
| 損耗因數(shù) (1MHz) | 0.0071 | ASTM D-150 | |
| 介電常數(shù) (1MHz) | 2.7 | ASTM D-150 | |
| 表面電阻 | 1.0E+16 | Ohm-cm | ASTM D-257 |
| 維卡軟化點(diǎn) | 112 | ℃ | ASTM D-1525 |
| 阻燃性 | V-0 | UL-94 | |
| UL長(zhǎng)期使用溫度 (無(wú)沖擊) | 85 | ℃ | UL-746B |
| 線膨脹系數(shù) | - | 1/℃ | E831 |
| 熱變形溫度 | ASTM D-648 | ||
| (1.8Mpa) | 93 | ℃ | |
| (0.45Mpa) | 101 | ℃ | |
| UL長(zhǎng)期使用溫度 (含沖擊) | ℃ | ℃ | UL-746B |
| 阻燃性 | 1.6 | mm | UL-94 |