| 比重 | 1.22 | ASTM D792 | |
| 成型收縮率 | SABIC Method | ||
| (flow, 3.2 mm) | 0.3-0.5 | % | |
| (xflow, 3.2 mm) | 0.4-0.6 | % | |
| 熔體流動速率 (260℃/2.16kgf) | 16.4 | g/10min | ASTM D1238 |
| 屈服拉伸強度 (5mm/min) | 640 | kgf/cm | ASTM D638 |
| 斷裂拉伸強度 (5mm/min) | 490 | kgf/cm | ASTM D638 |
| 屈服拉伸應變 (5mm/min) | 3.6 | % | ASTM D638 |
| 斷裂拉伸應變 (5mm/min) | 80 | % | ASTM D638 |
| 拉伸模量 (5mm/min) | 35800 | kgf/cm | ASTM D638 |
| 彎曲強度 (1.3mm/min,50mm span) | 1080 | kgf/cm | ASTM D790 |
| 彎曲模量 (1.3mm/min,50mm span) | 32000 | kgf/cm | ASTM D790 |
| IZOD無缺口沖擊強度 (23℃) | 190 | cm-kgf/cm | ASTM D4812 |
| IZOD缺口沖擊強度 (23℃) | 17 | cm-kgf/cm | ASTM D256 |
| 維卡軟化溫度 | 101 | ℃ | ASTM D1525 |
| 熱變形溫度 | ASTM D648 | ||
| (0.45Mpa,未退火) | 92 | ℃ | |
| (1.82Mpa,未退火) | 82 | ℃ | |
| 熱膨脹系數(shù) | ASTM E 831 | ||
| (-40℃to 40℃) | 5.94E-05 | 1/℃ | |
| (-40℃to 40℃) | 6.66E-05 | 1/℃ | |
| 相對溫度指數(shù) | 60 | ℃ | UL 746B |
| 阻燃性 | UL94 | ||
| (1.19mm) | V-0 | ||
| (1.98mm) | 5VB |