| 模具收縮率 (3.2mm) | 5-7 | E-3 | ASTM D-955 |
| 比重 | 1.15 | ASTM D-792 | |
| 吸水率 | - | % | ASTM D-570 |
| 彎曲強(qiáng)度 | 88 | Mpa | ASTM D-790 |
| 洛氏硬度 | - | R | ASTM D-785 |
| 彎曲模量 | 2343 | Mpa | ASTM D-790 |
| 拉伸模量 | 2274 | Mpa | ASTM D-638 |
| 沖擊強(qiáng)度缺口 (23℃) | 640 | J/m | ASTM D-256 |
| 拉伸強(qiáng)度(屈伏點(diǎn)) | 61 | Mpa | ASTM D-638 |
| 損耗因數(shù) (1MHz) | - | ASTM D-150 | |
| 拉伸率(斷裂點(diǎn)) | 150 | % | ASTM D-638 |
| 介電常數(shù) (1MHz) | - | ASTM D-150 | |
| 表面電阻 | - | Ohm-cm | ASTM D-257 |
| 體積電阻 | - | Ohm-cm | ASTM D-257 |
| UL長(zhǎng)期使用溫度 (無(wú)沖擊) | 60 | ℃ | UL-746B |
| 線膨脹系數(shù) (1/℃) | 7.2E-05 | E-831 | |
| 熱變形溫度 (1.8Mpa) | 112 | ℃ | ASTM D-648 |
| UL長(zhǎng)期使用溫度 (含沖擊) | 60 | ℃ | UL-746B |
| 阻燃性 | HB | UL-94 | |
| 熱變形溫度 (0.45Mpa) | 129 | ℃ | ASTM D-648 |
| 阻燃性 | 1.6 | mm | UL-94 |
| 維卡軟化點(diǎn) | - | ℃ | ASTM D-1525 |