| 比重 | 1.18 | ASTM D-792 | |
| 吸水率 | 0.1 | % | ASTM D-570 |
| 模具收縮率 (3.2mm) | 4-6 | E-3 | ASTM D-955 |
| 彎曲強(qiáng)度 | 102 | Mpa | ASTM D-790 |
| 彎曲模量 | 2653 | Mpa | ASTM D-790 |
| 洛氏硬度 | 123 | R | D785 |
| 沖擊強(qiáng)度缺口 (23℃) | 533 | J/m | ASTM D-256 |
| 拉伸模量 | - | Mpa | ASTM D-638 |
| 拉伸強(qiáng)度(屈伏點(diǎn)) | 63 | Mpa | ASTM D-638 |
| 拉伸率(斷裂點(diǎn)) | 40 | % | ASTM D-638 |
| 體積電阻 | 1.0E+17 | Ohm-cm | ASTM D-150 |
| 表面電阻 | 1.0E+16 | Ohm-cm | ASTM D-257 |
| 介電常數(shù) (1MHz) | - | ASTM D-150 | |
| 損耗因數(shù) (1MHz) | - | ASTM D-150 |
| 阻燃性 | 1.6 | mm | UL-94 |
| 線膨脹系數(shù) | - | 1/℃ | E-831 |
| 熱變形溫度 (0.45Mpa) | 104 | ℃ | ASTM D-648 |
| UL長(zhǎng)期使用溫度 (含沖擊) | 75 | ℃ | UL-746B |
| 維卡軟化點(diǎn) | 112 | ℃ | ASTM D-1525 |
| 阻燃性 | V-0 | UL-94 | |
| UL長(zhǎng)期使用溫度 (無(wú)沖擊) | 85 | ℃ | UL-746B |
| 熱變形溫度 (1.8Mpa) | 95 | ℃ | ASTM D-648 |