| 模具收縮率 (3.2mm) | 5-7 | E-3 | ASTM D-955 |
| 比重 | 1.14 | ASTM D-792 | |
| 吸水率 | - | % | ASTM D-570 |
| 拉伸強度(屈伏點) | 59 | Mpa | ASTM D-638 |
| 拉伸模量 | 2205 | Mpa | ASTM D-638 |
| 洛氏硬度 | - | R | ASTM D-785 |
| 沖擊強度缺口 (23℃) | 640 | J/m | ASTM D-256 |
| 彎曲強度 | 87 | Mpa | ASTM D-790 |
| 拉伸率(斷裂點) | 75 | % | ASTM D-638 |
| 彎曲模量 | 2377 | Mpa | ASTM D-790 |
| 表面電阻 | - | Ohm-cm | ASTM D-257 |
| 損耗因數(shù) (1MHz) | - | ASTM D-150 | |
| 體積電阻 | - | Ohm-cm | ASTM D-257 |
| 介電常數(shù) (1MHz) | - | ASTM D-150 |
| UL長期使用溫度 | UL-746B | ||
| (無沖擊) | 60 | ℃ | |
| (含沖擊) | 60 | ℃ | |
| 熱變形溫度 | ASTM D-648 | ||
| (1.8Mpa) | 110 | ℃ | |
| (0.45Mpa) | 126 | ℃ | |
| 阻燃性 | UL-94 | ||
| 1.5 | mm | ||
| HB | |||
| 線膨脹系數(shù) | - | 1/℃ | ASTM E-831 |
| 維卡軟化點 | - | ℃ | ASTM D-1525 |