| 比重 | 1.14 | ASTM D-792 | |
| 模具收縮率 (3.2mm) | 5-7 | E-3 | ASTM D-955 |
| 吸水率 | 0.1 | % | ASTM D-570 |
| 洛氏硬度 | - | R | ASTM D-785 |
| 沖擊強度缺口 (23℃) | 640 | J/m | ASTM D-256 |
| 拉伸率(斷裂點) | 150 | % | ASTM D-638 |
| 彎曲強度 | 86 | Mpa | ASTM D-790 |
| 拉伸強度(屈伏點) | 56 | Mpa | ASTM D-638 |
| 彎曲模量 | 2343 | Mpa | ASTM D-790 |
| 拉伸模量 | 2205 | Mpa | ASTM D-638 |
| 體積電阻 | - | Ohm-cm | ASTM D-257 |
| 損耗因數(shù) (1MHz) | - | ASTM D-150 | |
| 表面電阻 | - | Ohm-cm | ASTM D-257 |
| 介電常數(shù) (1MHz) | - | ASTM D-150 |
| 熱變形溫度 (1.8Mpa) | 107 | ℃ | ASTM D-648 |
| 阻燃性 | HB | UL-94 | |
| 維卡軟化點 | - | ℃ | ASTM D-1525 |
| 熱變形溫度 (0.45Mpa) | 123 | ℃ | ASTM D-648 |
| UL長期使用溫度 (無沖擊) | 60 | ℃ | UL-746B |
| 阻燃性 | 1.5 | mm | UL-94 |
| 線膨脹系數(shù) | 7.2E-05 | 1/℃ | E831 |
| UL長期使用溫度 (含沖擊) | 60 | ℃ | UL-746B |