| 模具收縮率 (3.2mm) | 4-6 | E-3 | ASTM D-955 |
| 比重 | 1.17 | ASTM D-792 | |
| 吸水率 | 0.1 | % | ASTM D-570 |
| 拉伸率(斷裂點) | 50 | % | ASTM D-638 |
| 拉伸強度(屈伏點) | 59 | Mpa | ASTM D-638 |
| 沖擊強度缺口 (23℃) | 427 | J/m | ASTM D-256 |
| 拉伸模量 | 2687 | Mpa | ASTM D-638 |
| 洛氏硬度 | 120 | R | ASTM D-785 |
| 彎曲強度 | 96 | Mpa | ASTM D-790 |
| 彎曲模量 | 2687 | Mpa | ASTM D-790 |
| 介電常數(shù) (1MHz) | - | ASTM D-150 | |
| 表面電阻 | 1.0E+14 | Ohm-cm | ASTM D257 |
| 損耗因數(shù) (1MHz) | - | ASTM D-150 | |
| 體積電阻 | 1.0E+17 | Ohm-cm | ASTM D-257 |
| UL長期使用溫度 (無沖擊) | 60 | ℃ | UL-746B |
| 維卡軟化點 | 90 | ℃ | ASTM D-1525 |
| 阻燃性 | 1.5 | mm | UL-94 |
| 線膨脹系數(shù) | - | 1/℃ | E-831 |
| 熱變形溫度 (0.45Mpa) | - | ℃ | ASTM D-648 |
| 阻燃性 | V-0 | UL-94 | |
| 熱變形溫度 (1.8Mpa) | 80 | ℃ | ASTM D-648 |
| UL長期使用溫度 (含沖擊) | 60 | ℃ | UL-746B |