| 特性 | 抗劃傷性高 耐氣候影響性能良好 |
| 用途 | 室外應(yīng)用 |
| 加工方法 | 共擠出成型 |
| 比重 | 1.12 | g/cm3 | ASTM D792 |
| 熔流率（熔體流動(dòng)速率）(220°C/10.0 kg) | 12 | g/10 min | ASTM D1238 |
| 收縮率 - 流動(dòng)(3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
| 洛氏硬度(R級(jí)) | 103 | ASTM D785 |
| 拉伸模量1(3.20 mm) | 1960 | MPa | ASTM D638 |
| 抗張強(qiáng)度2(屈服, 3.20 mm) | 44.1 | MPa | ASTM D638 |
| 伸長(zhǎng)率3 | ASTM D638 | ||
| 屈服, 3.20 mm | > 6.0 | % | ASTM D638 |
| 斷裂, 3.20 mm | 25 | % | ASTM D638 |
| 彎曲模量4(3.20 mm) | 2060 | MPa | ASTM D790 |
| 彎曲強(qiáng)度5(屈服, 3.20 mm) | 71.6 | MPa | ASTM D790 |
| 懸壁梁缺口沖擊強(qiáng)度 | ASTM D256 | ||
| -30°C, 3.20 mm | 39 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 39 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 180 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 130 | J/m | ASTM D256 |
| 載荷下熱變形溫度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 82.0 | °C | ASTM D648 |
| 維卡軟化溫度 | 90.0 | °C | ASTM D15256 |
| UL 阻燃等級(jí) | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| 干燥溫度 | 80.0 到 90.0 | °C | |
| 干燥時(shí)間 | 2.0 到 3.0 | hr | |
| 建議的大水分含量 | 0.010 | % | |
| 料筒1區(qū)溫度 | 190 到 200 | °C | |
| 料筒2區(qū)溫度 | 200 到 220 | °C | |
| 料筒3區(qū)溫度 | 210 到 230 | °C | |
| 料筒4區(qū)溫度 | 210 到 230 | °C | |
| 接頭溫度 | 210 到 230 | °C | |
| 熔體溫度 | 200 到 230 | °C | |
| 口模溫度 | 210 到 250 | °C |