| 吸收率 (23℃,60%RH) | 0.22 | % | ASTM D-570 |
| 比重 | 1.41 | ASTM D-792 |
| 洛氏硬度 | M75 | M scale | ASTM D-785 |
| 伸縮率 (23℃) | 8 | % | ASTM D-638 |
| 拉伸沖擊強度 (3.2mmt Stype) | 25 | kgf.cm/cm | ASTM D-1822 |
| 彎曲強度 (23℃) | 650 | kgf/cm | ASTM D-790 |
| IZ0D沖擊強度 (Notch 3.2mmt) | 5 | kgf.cm/cm | ASTM D-256 |
| 曲折彈性率 (23℃) | 2.50 | ×10kgf/cm | ASTM D-790 |
| 拉伸強度 (23℃) | 390 | kgf/cm | ASTM D-696 |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 表面電阻率 | ×10 | Ω | ASTM D-257 |
| 線膨脹系數(shù) (20℃-80℃) | 13 | ×10-5cm/cm/°C | ASTM D-696 |
| 熔點 (10℃/min) | 165 | ℃ | DSC Method |
| 熱變形溫度 | ASTM D-648 | ||
| 153 | ℃ | ||
| 102 | ℃ | ||
| 燃燒性 (0.8mmt) | HB | UL 94 | |
| 熔體流動速率 | 11 | g/10min | ASTM D-1238 |
| 成型收縮率 (3mmt,直徑100mm) | 1.6 | % |