| 吸水率 (23°C,60%RH) | 0.20 | % | ASTM D-570 |
| 成型收縮率 (3mmt,直徑100mm) | 1.6 | % |
| 填充材料含有率 | 25 | % | |
| 比重 | 1.59 | ASTM D-792 |
| 彎曲強度 (23°C) | 900 | kgf/cm | ASTM D-790 |
| 伸縮率 (23°C) | 10 | % | ASTM D-638 |
| IZOD沖擊強度 (Notch 3.2mmt) | 4.0 | kgf.cm/cm | ASTM D-256 |
| 斷裂強度 (2mmt) | 570 | kgf/cm | ASTM D-732 |
| 拉伸強度 (23°C) | 620 | kgf/cm | ASTM D-638 |
| 洛氏硬度 (M scale) | M83 | ASTM D-785 | |
| 曲折彈性率 (23°C) | 3.50 | ×104kgf/cm | ASTM D-790 |
| 耐電壓 | 20 | KV/mm | ASTM D-149 |
| 表面電阻率 (Ω) | 1×10 | ASTM D-257 | |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 線膨脹系數(shù) (20°C -80°C) | 9 | ×10-5cm/cm/°C | ASTM D-696 |
| 熔融指數(shù) | 8 | g/10 min | ASTM D-1238 |
| 熱變形溫度 (4.6kgf/cm) | 162 | °C | ASTM D-648 |
| 熔點 (10°C/min) | 165 | °C | DSC Method |
| 熱變形溫度 (18.6kgf/cm) | 135 | °C | ASTM D-648 |
| 燃燒性 (0.8mmt) | HB | UL-94 |