| 比重 | 1.51 | ASTM D-792 | |
| 吸收率 (23℃ 60%RH) | 0.18 | % | ASTM D-570 |
| 熔體流動速率 | 5 | g/10min | ASTM D-1238 |
| 伸長率 (23℃) | 15 | % | ASTM D-638 |
| 成型收縮率 (t3mm 直徑100mm) | 2.1 | % |
| 拉伸沖擊強(qiáng)度 (t3.2mm Stype) | 40 | kgf.cm/cm | ASTM D-1822 |
| 拉伸強(qiáng)度 (23℃) | 440 | kgf/cm | ASTM D-638 |
| 斷裂強(qiáng)度 (t2mm) | 421 | kgf/cm | ASTM D-732 |
| IZOD缺口沖擊強(qiáng)度 (Notch t3.2mm) | 4.0 | kgf.cm/cm | ASTM D-256 |
| 洛氏硬度 | 70 | M | ASTM D-785 |
| 彎曲彈性率 (23℃) | 2.00×104 | kgf/cm | ASTM D-790 |
| 彎曲強(qiáng)度 (23℃) | 650 | kgf/cm | ASTM D-790 |
| 耐電壓 | 16 | KV/mm | ASTM D-149 |
| 導(dǎo)電率 (10Hz) | 3.1 | ASTM D-150 | |
| 體積電阻率 | 1×1014 | Ω.cm | ASTM D-257 |
| 個質(zhì)損耗系數(shù) (10Hz) | 0.009 | ASTM D-150 | |
| 表面電阻率 | 1×1016 | Ω | ASTM D-257 |
| 熱變形溫度 (4.6kgf/cm) | 156 | ℃ | ASTM D-648 |
| 熔點 (10℃/min) | 165 | ℃ | DSC Method |
| 熱變形溫度 (18.6kgf/cm) | 106 | ℃ | ASTM D-648 |
| 線性膨脹系數(shù) (20℃ -80℃) | 13×10-5 | mm/mm/℃ | ASTM D-696 |
| 阻燃性 (t0.8mm) | HB | UL-94 |