| 熔體流動速率 | 3 | g/10 min | ASTM D-1238 |
| 吸收率 (23°C,60%RH) | 0.36 | % | ASTM D-570 |
| 比重 | 1.29 | ASTM D-792 | |
| 成型收縮率 (t3mm,直徑100mm) | 1.2 | % | |
| 填充材料含有率 | Super | % |
| 曲折彈性率 (23℃) | 0.66 | ×10kgf/cm | ASTM D-790 |
| 拉伸強(qiáng)度 (23℃) | 240 | kgf/cm | ASTM D-638 |
| 伸縮率 (23℃) | >300 | % | ASTM D-638 |
| IZOD沖擊強(qiáng)度 (Notch t3.2mm) | >100 | kgf.cm/cm | ASTM D-256 |
| 洛氏硬度 (M scale) | M64 | ASTM D-785 | |
| 拉伸沖擊強(qiáng)度 (t3.2mm S type) | >=300 | kgf.cm/cm | ASTM D-1822 |
| 彎曲強(qiáng)度 (23℃) | 260 | kgf/cm | ASTM D-790 |
| 表面電阻率 | 1×10 | Ω | ASTM D-257 |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 線膨脹系數(shù) (20C°-80C°) | 13 | ×10-5cm/cm/℃ | ASTM D-696 |
| 熔點 (10C°/min) | 165 | ℃ | DSC Method |
| 熱變形溫度 (×10-5cm/cm/℃) | 70 | ℃ | ASTM D-648 |
| 燃燒性 (t0.8mm) | HB | UL 94 | |
| 熱變形溫度 (4.6kgf/cm) | 125 | ℃ | ASTM D-648 |