| 吸收率 (23℃,60%RH) | 0.20 | % | ASTM D-570 |
| 熔體流動(dòng)速率 | 6 | g/10min | ASTM D-1238 |
| 比重 | 1.64 | ASTM D-792 |
| 曲折彈性率 (23℃) | 9.50 | ×10kgf/cm | ASTM D-790 |
| 伸縮率 (23℃,60%RH) | 2 | % | ASTM D-638 |
| 拉伸強(qiáng)度 (23℃) | 1330 | kgf/cm | ASTM D-638 |
| 洛氏硬度 | M95 | M scale | ASTM D-785 |
| 拉伸沖擊強(qiáng)度 (3.2mmt Stype) | 175 | kgf.cm/cm | ASTM D-1822 |
| 彎曲強(qiáng)度 (23℃) | 1900 | kgf/cm | ASTM D-790 |
| IZOD沖擊強(qiáng)度 (Notch 3.2mmt) | 8 | kgf.cm/cm | ASTM D-256 |
| 表面電阻率 | 1×10 | Ω | ASTM D-257 |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 成型收縮率 (3mmt,直徑100mm) | 0.2 | % |
| 熱變形溫度 (18.6kgf/cm) | 163 | °C | ASTM D-648 |
| 熔點(diǎn) (10℃/min) | 165 | ℃ | DSC Method |
| 熱變形溫度 (4.6kgf/cm) | 164 | ℃ | ASTM D-648 |
| 燃燒性 (0.8mmt) | HB | UL 94 | |
| 線膨脹系數(shù) (20℃-80℃) | 13 | ×10-5cm/cm/℃ | ASTM D-696 |