| 比重 | 1.63 | g/cm3 | ASTM D792 |
| 熔體質(zhì)量流動速率 (190℃/2.16kg) | 18 | g/10 min | ASTM D1238 |
| 成型收縮率 (flow,2.00MM) | 1.5 | % | ASTM D955 |
| 吸水率 (E,23℃,60%rh) | 0.20 | % | ASTM D570 |
| 拉伸強度 (Yield,23℃) | 57.0 | MPa | ASTM D638 |
| 拉伸伸長率 (Break,23℃) | 4.0 | % | ASTM D638 |
| 彎曲模量 (23°C) | 4040 | MPa | ASTM D790 |
| 彎曲強度 (Yield,23℃) | 96.0 | MPa | ASTM D790 |
| IZOD缺口沖擊強度 (3.20mm) | 37.0 | J/m | ASTM D256 |
| 表面電阻率 | 1.0E+16 | ohms | ASTM D257 |
| 體積電阻率 | 1.0E+14 | ohm·cm | ASTM D257 |
| 熱畸變溫度 (1.8MPa,未退火) | 138 | °C | ASTM D648 |
| 熔融溫度 | 165 | °C | DSC |
| 阻燃等級 (0.8mm) | HB | UL 94 |