| 吸水率 (23℃.60%RH) | 0.20 | % | ASTM D-570 |
| 熔體流動速率 | 9 | g/10min | ASTM D-1238 |
| 填充材料含有率 | 25 | % | |
| 比重 | 1.59 | ASTM D-792 |
| 伸縮率 (23℃) | 3 | % | ASTM D-638 |
| 拉伸強(qiáng)度 (23℃) | 1450 | kgf/cm | ASTM D-638 |
| 彎曲強(qiáng)度 (23℃) | 2100 | kgf/cm | ASTM D-790 |
| 拉伸沖擊強(qiáng)度 (3.2mmt Stype) | 180 | kgf.cm/cm | ASTM D-1822 |
| 曲折彈性率 (23℃) | 8.80 | ×10kgf/cm | ASTM D-790 |
| 斷裂強(qiáng)度 (2mmt) | 760 | kgf/cm | ASTM D-732 |
| IZOD沖擊強(qiáng)度 (Notch 3.2mmt) | 10 | kgf.cm/cm | ASTM D-256 |
| 洛氏硬度 (M scale) | M95 | ASTM D-785 |
| 耐電壓 | 23 | KV/mm | ASTM D-149 |
| 表面電阻率 | 1×10 | Ω | ASTM D-257 |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 成型收縮率 (3mmt,直徑100mm) | 0.5 | % |
| 燃燒性 (0.8mmt) | HB | UL 94 | |
| 熔點 (10℃/min) | 165 | oC | DSC Method |
| 線膨脹系數(shù) (20oC-80oC) | 2-3 | ×10-5cm/cm/°C | ASTM D-696 |
| 熱變形溫度 | ASTM D-648 | ||
| (18.6kgf/cm) | 163 | oC | |
| (4.6kgf/cm) | 164 | oC |