| 熔體流動速率 | 9 | g/10min | ASTM D-1238 |
| 吸收率 (23℃ 60%RH) | 0.22 | % | ASTM D-570 |
| 比重 | 1.44 | ASTM D-792 | |
| 伸長率 (23℃) | 30 | % | ASTM D-638 |
| 成型收縮率 (t3mm 直徑100mm) | 2.0 | % |
| 彎曲強度 (23℃) | 880 | kgf/cm | ASTM D-790 |
| 拉伸強度 (23℃) | 630 | kgf/cm | ASTM D-638 |
| 彎曲彈性率 (23℃) | 2.70×104 | kgf/cm | ASTM D-790 |
| 拉伸沖擊強度 (t3.2mm Stype) | 90 | kgf.cm/cm | ASTM D-1822 |
| IZOD缺口沖擊強度 (Notch t3.2mm) | 5.5 | kgf.cm/cm | ASTM D-256 |
| 洛氏硬度 | 80 | M | ASTM D-785 |
| 表面電阻率 | 1×1016 | Ω | ASTM D-257 |
| 體積電阻率 | 1×1014 | Ω.cm | ASTM D-257 |
| 阻燃性 (t0.8mm) | HB | UL-94 | |
| 線性膨脹系數(shù) (20℃ -80℃) | 13×10-5 | mm/mm/℃ | ASTM D-696 |
| 熔點 (10℃/min) | 165 | ℃ | DSC Method |
| 熱變形溫度 | ASTM D-648 | ||
| (18.6kgf/cm) | 110 | ℃ | |
| (4.6kgf/cm) | 158 | ℃ |