| 比重 | 1.41 | g/cm3 | ASTM D792, ISO 1183 |
| 熔體質(zhì)量流動(dòng)速率 | |||
| 2.5 | g/10 min | ASTM D1238 | |
| 3.0 | g/10 min | ISO 1133 | |
| 成型收縮率 | |||
| (flow,3.00MM) | 2.0 | % | ASTM D955 |
| (3.00mm) | 2.2 | % | ISO 294-4 |
| 吸水率 (E,23℃,60%rh) | 0.22 | % | ASTM D570 |
| 拉伸強(qiáng)度 | |||
| (Yield,23℃) | 64.0 | MPa | ASTM D638 |
| (Yield,23℃) | 69.0 | MPa | ISO 527-2 |
| 拉伸伸長(zhǎng)率 (Break,23℃) | 40 | % | ASTM D638, ISO 527-2 |
| 彎曲模量 | |||
| (23°C) | 2660 | MPa | ASTM D790 |
| (23°C) | 2700 | MPa | ISO 178 |
| 彎曲強(qiáng)度 | |||
| (23°C) | 92.0 | MPa | ISO 178 |
| (23°C) | 86.0 | MPa | ASTM D790 |
| Charpy無(wú)缺口沖擊強(qiáng)度 | 12 | kJ/m2 | ISO 179/1eA |
| IZOD缺口沖擊強(qiáng)度 (3.20mm) | 69.0 | J/m | ASTM D256 |
| 表面電阻率 | 1.0E+14 | ohms | IEC 60093 |
| 體積電阻率 | 1.0E+12 | ohm·cm | IEC 60093 |
| 電氣強(qiáng)度 | 19 | kV/mm | IEC 60243-1 |
| 熱變形溫度 (1.8MPa,未退火) | 100 | °C | ISO 75-2/A |
| 熔融溫度 | 165 | °C | |
| 線性熱膨脹系數(shù) (flow,20 to 80°C) | 0.00013 | cm/cm/°C | ASTM D696 |
| 阻燃等級(jí) (0.8mm) | HB | UL 94 |