| 吸水率 (23.C 60%RH) | 0.22 | % | ASTM D-570 |
| 熔體流動速率 | 9 | G/10min | ASTM D-1237 |
| 比重 | 1.41 | ASTM D-792 |
| 拉伸強度 (1.6mm) | 98 | KJ/m | ASTM D-1822 |
| 拉伸長度 (23℃) | 50 | % | ASTM D-638 |
| 拉伸強度 (23℃) | 62.3 | MPa | ASTM D-638 |
| 撓曲強度 (23℃) | 91.2 | MPa | ASTM D-790 |
| 洛氏硬度 | 80 | M scale | ASTM D-785 |
| IZOD沖擊強度 (3.2mm) | 54 | J/m | ASTM D-256 |
| 彎曲模量 (23℃) | 2.62 | GPa | ASTM D-790 |
| 撕裂強度 (2mm) | 54.9 | MPa | ASTM D-732 |
| 體積電阻系數(shù) | 1×1014/ | ASTM D-257 | |
| 介電常數(shù) (10Hz) | 33 | Pf/m | ASTM D-150 |
| 表面電阻系數(shù) | 1×10 | ASTM D-257 | |
| 介電損耗正切 (10Hz) | 0.007 | ASTM D-150 | |
| 耐電壓 | 19 | MV/m | ASTM D-149 |
| 成型收縮率 (平行方向) | 20 | % |
| 燃燒性 | HB | UL 94 | |
| 熔點 (10℃/min) | 165 | ℃ | DSC |
| 負荷撓曲溫度 | ASTM D-648 | ||
| (455kPa) | 158 | ℃ | |
| (820kPa) | 110 | ℃ | |
| 線膨脹系數(shù) (20℃-80℃) | 13 | 10 |