| 比重 | 1.41 | g/cm3 | ASTM D792, ISO 1183 |
| 熔體質(zhì)量流動(dòng)速率 | 13 | g/10 min | ASTM D792, ISO 1183 |
| 成型收縮率 | |||
| (flow,3.00MM) | 2.0 | % | ASTM D955 |
| (3.00mm) | 2.0 | % | ISO 294-4 |
| 吸水率 (E,23℃,60%rh) | 0.22 | % | ASTM D570 |
| 洛氏硬度 (M-Scale) | 82 | ASTM D785 |
| 拉伸強(qiáng)度 | |||
| (Yield,23℃) | 65.0 | MPa | ASTM D638 |
| (Yield,23℃) | 70.0 | MPa | ISO 527-2 |
| 拉伸伸長率 | |||
| (Break,23℃) | 55 | % | ASTM D638 |
| (Break,23℃) | 30 | % | ISO 527-2 |
| 彎曲模量 | |||
| (23°C) | 2790 | MPa | ASTM D790 |
| (23°C) | 2800 | MPa | ISO 178 |
| 彎曲強(qiáng)度 | |||
| (23°C) | 93.0 | MPa | ASTM D790 |
| (23°C) | 94.0 | MPa | ISO 178 |
| 剪切強(qiáng)度 (2.00mm) | 56.0 | MPa | ASTM D732 |
| 夏比缺口沖擊強(qiáng)度 | 7.5 | kJ/m2 | ISO 179/1eA |
| IZOD缺口沖擊強(qiáng)度 (3.20mm) | 69.0 | J/m | ASTM D256 |
| 表面電阻率 | |||
| 1.0E+16 | ohms | ASTM D257 | |
| 1.0E+14 | ohms | IEC 60093 | |
| 體積電阻率 | |||
| 1.0E+14 | ohm·cm | ASTM D257 | |
| 1.0E+12 | ohm·cm | IEC 60093 | |
| 電氣強(qiáng)度 | 19 | kV/mm | ASTM D149, IEC 60243-1 |
| 介電常數(shù) (1E+6 Hz) | 3.70 | ASTM D150 | |
| 介質(zhì)損耗因數(shù) (1E+6 Hz) | 0.0070 | ASTM D150 |
| 熱畸變溫度 | ASTM D648 | ||
| (0.45MPa,未退火) | 158 | °C | |
| (1.8MPa,未退火) | 112 | °C | |
| (1.8MPa,未退火) | 110 | °C | |
| 熔融溫度 | 165 | °C | DSC |
| 線性熱膨脹系數(shù) (flow,20 to 80°C) | 0.00013 | cm/cm/°C | ASTM D696 |
| 阻燃等級(jí) (0.8mm) | HB | UL 94 |