| 成型收縮率 (3mmt,直徑100mm) | 2.0 | % | |
| 吸水率 (23°C,60%RH) | 0.22 | % | ASTM D-570 |
| 比重 | 1.41 | ASTM D-792 |
| 斷裂強(qiáng)度 (2mmt) | 560 | kgf/cm | ASTM D-732 |
| 拉伸強(qiáng)度 (23℃) | 590 | kgf/cm | ASTM D-638 |
| 伸縮率 (23℃) | 40 | % | ASTM D-638 |
| 洛氏硬度 (M scale) | M80 | ASTM D-785 | |
| 曲折彈性率 (23°C) | 2.60 | ×10kgf/cm | ASTM D-790 |
| 拉伸沖擊強(qiáng)度 (3.2mmt Stype) | 90 | kgf.cm/cm | ASTM D-1822 |
| 彎曲強(qiáng)度 (23℃) | 850 | kgf/cm | ASTM D-790 |
| IZ0D沖擊強(qiáng)度 (Notch 3.2mmt) | 5.5 | kgf.cm/cm | ASTM D-256 |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 表面電阻率 | 1×10 | Ω | ASTM D-257 |
| 導(dǎo)電率 (10Hz) | 3.7 | ASTM D-150 | |
| 個(gè)質(zhì)損耗系數(shù) (10Hz) | 0.007 | ASTM D-150 | |
| 耐電壓 | 19 | KV/mm | ASTM D-149 |
| 線膨脹系數(shù) (20°C-80°C) | 13 | ×10-5cm/cm/°C | ASTM D-696 |
| 熔點(diǎn) (10°C/min) | 165 | °C | DSC Method |
| 燃燒性 (0.8mmt) | HB | UL-94 | |
| 熱變形溫度 | ASTM D-648 | ||
| (18.6kgf/cm) | 110 | °C | |
| (4.6kgf/cm) | 158 | °C | |
| 熔融指數(shù) | 28 | g/10 min |