| 比重 | 1.62 | g/cm3 | ASTM D792 |
| 熔體質(zhì)量流動(dòng)速率 (190℃/2.16kg) | 6.5 | g/10 min | ASTM D1238 |
| 吸水率 (E,23℃,60%rh) | 0.20 | % | ASTM D570 |
| 拉伸強(qiáng)度 (Yield,23℃) | 157 | MPa | ASTM D638 |
| 拉伸伸長率 (Yield,23℃) | 2.0 | % | ASTM D638 |
| 彎曲模量 (23°C) | 9590 | MPa | ASTM D790 |
| 彎曲強(qiáng)度 (23°C) | 216 | MPa | ASTM D790 |
| IZOD缺口沖擊強(qiáng)度 (3.20mm) | 95.0 | J/m | ASTM D256 |
| 表面電阻率 | 1.0E+16 | ohms | ASTM D257 |
| 體積電阻率 | 1.0E+14 | ohm·cm | ASTM D257 |
| 熱畸變溫度 (1.8MPa,未退火) | 164 | °C | ASTM D648 |
| 熔融溫度 | 165 | °C | ASTM D3418 |
| 阻燃等級(jí) (0.8mm) | HB | UL 94 |