| 熔體流動(dòng)速率 (g/10 min) | 5 | ASTM D-1238 |
| 吸收率 (23°C,60%RH) | 0.25 | % | ASTM D-570 |
| 成型收縮率 (t3mm,直徑100mm) | 1.7 | % | |
| 填充材料含有率 | High | % | |
| 比重 | 1.36 | ASTM D-792 |
| 拉伸沖擊強(qiáng)度 (t3.2mm S type) | 220 | kgf.cm/cm | ASTM D-1822 |
| 拉伸強(qiáng)度 (23℃) | 380 | kgf/cm | ASTM D-638 |
| 彎曲強(qiáng)度 (23℃) | 490 | kgf/cm | ASTM D-790 |
| IZOD沖擊強(qiáng)度 (Notch t3.2mm) | 12 | kgf.cm/cm | ASTM D-256 |
| 伸縮率 (23℃) | >=200 | % | ASTM D-638 |
| 洛氏硬度 (M scale) | M77 | ASTM D-785 | |
| 曲折彈性率 (23℃) | 1.40 | ×10kgf/cm | ASTM D-790 |
| 表面電阻率 | 1×10 | Ω | ASTM D-257 |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 燃燒性 (t0.8mm) | HB | UL 94 | |
| 熱變形溫度 | ASTM D-648 | ||
| (18.6kgf/cm) | 88 | ℃ | |
| (4.6kgf/cm) | 143 | ℃ | |
| 熔點(diǎn) (10C°/min) | 165 | ℃ | DSC Method |
| 線膨脹系數(shù) (20C°-80C) | 13 | ×10-5cm/cm/℃ | ASTM D-696 |