| 比重 | 1.42 | ASTM D792 | |
| 吸水率 | 0.2 | % | ASTM D570 |
| 縮模率 | 旭化成法 | ||
| (平行方向) | 1.8-2.2 | % | |
| (垂直方向) | 1.8-2.2 | % |
| 拉伸強度 | 64 | MPa | ASTM D638 |
| 延伸率 | 80 | % | ASTM D638 |
| 彎曲強度 | 91 | MPa | ASTM D790 |
| 彎曲模量 | 2650 | MPa | ASTM D790 |
| IZOD缺口沖擊強度 | 118 | J/M | ASTM D256 |
| 洛氏硬度 | ASTM D785 | ||
| 92 | M | ||
| 120 | R | ||
| 磨耗 | 13 | ASTM D1044 |
| 熔融指數(shù) | 1.7 | g/10min | ASTM D1238 |
| 線膨脹系數(shù) | 10 | TMA法 | |
| 熱變形溫度 | ASTM D648 | ||
| (1.82MPa) | 125 | ℃ | |
| (0.45MPa) | 172 | ℃ | |
| 阻燃性 | HB |