| 熔體流動速率 | |||
| 34 | g/10min | ASTM D1238 | |
| (190℃/2.16kg) | 34 | g/10min | ISO 1133 |
| 吸水率 (24 hr) | 0.2 | % | ASTM D570 |
| 比重 | 1.42 | g/cm | ASTM D792,ISO 1183 |
| 成型收縮率 | |||
| (Flow) | 1.8-2.2 | % | ASTM D955,ISO 294-4 |
| (Across Flow) | 1.8-2.2 | % | ISO 294-4 |
| 洛氏硬度 | ASTM D785 | ||
| (M-Scale) | 94 | ||
| (R-Scale) | 120 |
| 拉伸模量 | 3400 | MPa | ISO 527-2 |
| 屈服拉伸應(yīng)力 | 73 | MPa | ISO 527-2 |
| 拉伸應(yīng)力 | 69 | MPa | ASTM D638 |
| 斷裂伸長率 | |||
| 30 | % | ASTM D638 | |
| 25 | % | ISO 527-2 | |
| 彎曲模量 | 3040 | MPa | ASTM D790 |
| 彎曲強(qiáng)度 | 108 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles) | 13 | mg | ASTM D1044 |
| CHARPY缺口沖擊強(qiáng)度 (23℃) | 7 | kJ/m | ISO 179/1eA |
| Izod 缺口沖強(qiáng)度 | 59 | J/m | ASTM D256 |
| 熱變形溫度 | |||
| (0.45MPa,unannealed) | 172 | ℃ | ASTM D648 |
| (0.45MPa,unannealed) | 165 | ℃ | ISO 75-2/B |
| (1.8MPa,unannealed) | 136 | ℃ | ASTM D648 |
| (1.8MPa,unannealed) | 100 | ℃ | ISO 75-2/A |
| 流動方向線性熱膨脹系數(shù) | 0.0001 | cm/cm/℃ | ASTM E831 |
| 阻燃等級 | HB | UL 94 |