| 比重 | 1.42 | g/cm3 | ASTM D792, ISO 1183 |
| 熔體質(zhì)量流動(dòng)速率 | |||
| 2.8 | g/10 min | ASTM D1238 | |
| (190℃/2.16kg) | 2.8 | g/10 min | ISO 1133 |
| 成型收縮率 | |||
| (flow) | 1.8 to 2.2 | % | ASTM D955, ISO 294-4 |
| (Across flow) | 1.8 to 2.2 | % | ISO 294-4 |
| 吸水率 (24hr) | 0.20 | % | ASTM D570 |
| 洛氏硬度 | ASTM D785 | ||
| (M-Scale) | 94 | ||
| (R-Scale) | 120 |
| 拉伸模量 | 3100 | MPa | ISO 527-2 |
| 拉伸應(yīng)力 | |||
| (Yield) | 71.0 | MPa | ISO 527-2 |
| 68.0 | MPa | ASTM D638 | |
| 拉伸伸長率 | |||
| (Break) | 75 | % | ASTM D638 |
| (Break) | 65 | % | ISO 527-2 |
| 彎曲模量 | 2740 | MPa | ASTM D790 |
| 彎曲強(qiáng)度 | 98.0 | MPa | ASTM D790 |
| 泰伯磨耗量 (1000次) | 13.0 | mg | ASTM D1044 |
| 夏比缺口沖擊強(qiáng)度 (23°C) | 13 | kJ/m2 | ISO 179/1eA |
| IZOD缺口沖擊強(qiáng)度 | 108 | J/m | ASTM D256 |
| 熱畸變溫度 | ASTM D648 | ||
| (0.45MPa,未退火) | 172 | °C | |
| (1.8MPa,未退火) | 133 | °C | |
| (0.45MPa,未退火) | 163 | °C | |
| (1.8MPa,未退火) | 96.0 | °C | |
| 線性熱膨脹系數(shù) (flow) | 0.00010 | cm/cm/°C | ASTM E831 |
| 阻燃等級(jí) | HB | UL 94 |