| 熔體流動速率 (190℃/2.16kg) | 9 | g/10min | ASTM D1238 |
| 吸水率 (Saturation) | 0.2 | % | ASTM D570 |
| 比重 | 1.41 | g/cm | ASTM D792 |
| 成型收縮率 (Flow) | 1.6-2 | % | ASTM D955 |
| 洛氏硬度 | ASTM D785 | ||
| (M-Scale) | 80 | ||
| (R-Scale) | 115 |
| 拉伸強度 | 60.8 | MPa | ASTM D638 |
| 斷裂伸長率 | 60 | % | ASTM D638 |
| 彎曲模量 | 2600 | MPa | ASTM D790 |
| 彎曲強度 | 88.3 | MPa | ASTM D790 |
| Izod 缺口沖強度 | 58.8 | J/m | ASTM D256 |
| 熱變形溫度 | ASTM D648 | ||
| (0.45MPa,unannealed) | 158 | ℃ | |
| (1.8MPa,unannealed) | 110 | ℃ | |
| 融化溫度 | 167 | ℃ | ASTM D648 |
| 流動方向線性熱膨脹系數(shù) | 0.0001 | cm/cm/℃ | ASTM D696 |
| 阻燃等級 | HB | UL 94 |