| 比重 | 1.46 | ASTM D792 | |
| 吸水率 | 0.2 | % | ASTM D570 |
| 縮模率 | 旭化成法 | ||
| (平行方向) | 0.1-0.2 | % | |
| (垂直方向) | 0.6-0.8 | % |
| 拉伸強度 | 147 | MPa | ASTM D638 |
| 延伸率 | 4 | % | ASTM D638 |
| 彎曲強度 | 196 | MPa | ASTM D790 |
| 彎曲模量 | 14210 | MPa | ASTM D790 |
| IZOD缺口沖擊強度 | 39 | J/M | ASTM D256 |
| 洛氏硬度 | 104 | M | ASTM D785 |
| 熔融指數(shù) | 4 | g/10min | ASTM D1238 |
| 線膨脹系數(shù) | 4/9 | TMA法 | |
| 熱變形溫度 | ASTM D648 | ||
| (1.82MPa) | 164 | ℃ | |
| (0.45MPa) | 166 | ℃ | |
| 阻燃性 | HB |