| 吸濕率 (濕) | 1.6 | % |
| 成型收縮率 (干) | 0.3/0.7 | % | 旭化成方法 |
| 比重 (干) | 1.50 | ASTM D-792 |
| 拉伸強(qiáng)度 (干(濕)) | 186(132) | MPa | ASTM D-638 |
| 抗撓強(qiáng)度 (干(濕)) | 304(177) | MPa | ASTM D-790 |
| 洛氏硬度 (干(濕)) | 118(-) | R scale | ASTM D-785 |
| 抗撓系數(shù) (干(濕)) | 11.0(5.9) | GPa | ASTM D-790 |
| 懸臂梁式缺口沖擊強(qiáng)度 (干(濕)) | 147(226) | J/M | ASTM D-256 |
| 洛氏硬度 (干(濕)) | 93(-) | M scale | ASTM D-785 |
| 斷裂延伸率 (干(濕)) | 3(4) | % | ASTM D-638 |
| 熱變形溫度 | ASTM D-648 | ||
| (0.46MPa,干) | 250 | ℃ | |
| (1.82MPa,干) | 240 | ℃ | |
| 阻燃性 (干) | HB |