| 吸濕率 (濕) | 2.3 | % |
| 比重 (干) | 1.16 | ASTM D-792 | |
| 成型收縮率 (干) | 0.9-1.6 | % | 旭化成方法 |
| 磨耗率 (濕) | 7 | ×10-6kg/1000times | ASTM D-1044 |
| 洛氏硬度 (干(濕)) | 120(110) | R scale | ASTM D-785 |
| 斷裂延伸率 (干(濕)) | 7(70) | % | ASTM D-638 |
| 懸臂梁式缺口沖擊強度 (干(濕)) | 29(58) | J/M | ASTM D-256 |
| 抗撓強度 (干(濕)) | 128(56) | MPa | ASTM D-790 |
| 抗撓系數(shù) (干(濕)) | 3.3(1.3) | GPa | ASTM D-790 |
| 洛氏硬度 (干(濕)) | 85(55) | M scale | ASTM D-785 |
| 拉伸強度 (干(濕)) | 83(58) | MPa | ASTM D-638 |
| 熱變形溫度 | ASTM D-648 | ||
| (0.46MPa,干) | 240 | ℃ | |
| (1.82MPa,干) | 80 | ℃ | |
| 阻燃性 (干) | V-0 | UL 94 | |
| 線性膨脹系數(shù) (干) | 7 | ×10-5/K | ASTM D-696 |
| 氧指數(shù) (干) | 36 | % | ASTM D-2863 |