| 吸濕率 (濕) | 1.9 | % |
| 比重 (干) | 1.39 | ASTM D-792 | |
| 成型收縮率 (干) | 0.4/0.9 | % | 旭化成方法 |
| 洛氏硬度 (干(濕)) | 120(110) | R scale | ASTM D-785 |
| 懸臂梁式缺口沖擊強(qiáng)度 (干(濕)) | 137(196) | J/M | ASTM D-256 |
| 抗撓系數(shù) (干(濕)) | 9.1(5.0) | GPa | ASTM D-790 |
| 抗撓強(qiáng)度 (干(濕)) | 289(167) | MPa | ASTM D-790 |
| 斷裂延伸率 (干(濕)) | 3(7) | % | ASTM D-638 |
| 拉伸強(qiáng)度 (干(濕)) | 181(118) | MPa | ASTM D-638 |
| 洛氏硬度 (干(濕)) | 93(68) | M scale | ASTM D-785 |
| 熱變形溫度 (1.82MPa,干) | 240 | ℃ | ASTM D-648 |
| 線性膨脹系數(shù) (干) | 3 | ×10-5/K | ASTM D-696 |
| 阻燃性 (干) | HB | UL 94 | |
| 熱變形溫度 (0.46MPa,干) | 250 | ℃ | ASTM D-648 |