| 吸濕率 (濕) | 2.1 | % |
| 成型收縮率 (干) | 0.7/1.2 | % | 旭化成方法 |
| 比重 (干) | 1.25 | ASTM D-792 | |
| 磨耗率 (濕) | 9 | ×10-6kg/1000times | ASTM D-1044 |
| 洛氏硬度 (干(濕)) | 120(-) | R scale | ASTM D-785 |
| 抗撓系數(shù) (干(濕)) | 4.9(2.5) | GPa | ASTM D-790 |
| 斷裂延伸率 (干(濕)) | 2.5(8) | % | ASTM D-638 |
| 抗撓強(qiáng)度 (干(濕)) | 167(108) | MPa | ASTM D-790 |
| 懸臂梁式缺口沖擊強(qiáng)度 (干(濕)) | 49(59) | J/M | ASTM D-256 |
| 拉伸強(qiáng)度 (干(濕)) | 108(79) | MPa | ASTM D-638 |
| 洛氏硬度 (干(濕)) | 94(71) | M scale | ASTM D-785 |
| 阻燃性 (干) | HB | UL 94 | |
| 線性膨脹系數(shù) (干) | 4 | ×10-5/K | ASTM D-696 |
| 熱變形溫度 | ASTM D-648 | ||
| (1.82MPa,干) | 240 | ℃ | |
| (0.46MPa,干) | 258 | ℃ |