| 吸濕率 (濕) | 2.2 | % |
| 比重 (干) | 1.14 | ASTM D-792 | |
| 磨耗率 (濕) | 6 | ×10-6kg/1000times | ASTM D-1044 |
| 成型收縮率 (干) | 0.9-1.6 | % | 旭化成方法 |
| 斷裂延伸率 (干(濕)) | 35(200) | % | ASTM D-638 |
| 拉伸強度 (干(濕)) | 88(67) | MPa | ASTM D-638 |
| 抗撓系數(shù) (干(濕)) | 3.0(1.3) | GPa | ASTM D-790 |
| 懸臂梁式缺口沖擊強度 (干(濕)) | 39(108) | J/M | ASTM D-256 |
| 抗撓強度 (干(濕)) | 128(59) | MPa | ASTM D-790 |
| 洛氏硬度 | ASTM D-785 | ||
| (干(濕)) | 120(110) | R scale | |
| (干(濕)) | 85(60) | M scale |
| 阻燃性 (干) | V-2 | UL 94 | |
| 導(dǎo)熱率 (干) | 0.2 | W/(m.k) | |
| 線性膨脹系數(shù) (干) | 8 | ×10-5/K | ASTM D-696 |
| 熱變形溫度 | ASTM D-648 | ||
| (0.46MPa,干) | 240 | ℃ | |
| (1.82MPa,干) | 75 | ℃ | |
| 比熱容 (干) | 1670 | J/(kg.k) |
| 氧指數(shù) (干) | 26 | % | ASTM D-2863 |