| 吸濕率 (濕) | 2.5 | % |
| 比重 (干) | 1.14 | ASTM D-792 | |
| 磨耗率 (濕) | 4 | ×10-6kg/1000times | ASTM D-1044 |
| 成型收縮率 (干) | 1.3-2.0 | % | 旭化成方法 |
| 抗撓強(qiáng)度 (干(濕)) | 118(54) | MPa | ASTM D-790 |
| 洛氏硬度 | ASTM D-785 | ||
| (干(濕)) | 120(105) | R scale | |
| (干(濕)) | 80(55) | M scale | |
| 懸臂梁式缺口沖擊強(qiáng)度 (干(濕)) | 49(245) | J/M | ASTM D-256 |
| 抗撓系數(shù) (干(濕)) | 2.8(1.2) | GPa | ASTM D-790 |
| 拉伸強(qiáng)度 (干(濕)) | 80(59) | MPa | ASTM D-638 |
| 斷裂延伸率 (干(濕)) | 100(300) | % | ASTM D-638 |
| 熱變形溫度 (1.82MPa,干) | 70 | ℃ | ASTM D-648 |
| 比熱容 (干) | 1670 | J/(kg.k) | |
| 導(dǎo)熱率 (干) | 0.2 | W/(m.k) | |
| 線性膨脹系數(shù) (干) | 8 | ×10-5/K | ASTM D-696 |
| 熱變形溫度 (0.46MPa,干) | 230 | ℃ | ASTM D-648 |
| 氧指數(shù) (干) | 23 | % | ASTM D-2863 |