| 拉伸應(yīng)力 | ASTM D 638 | ||
| (屈服 Type I 2.0 in/min) | 8800 | psi | |
| (斷裂 Type I 2.0 in/min) | 8100 | psi | |
| 拉伸應(yīng)變 | ASTM D 638 | ||
| (屈服 Type I 2.0 in/min) | 5 | % | |
| (斷裂 Type I 2.0 in/min) | 100 | % | |
| 拉伸模量 (0.2 in/min) | 343000 | psi | ASTM D 638 |
| 彎曲應(yīng)力 (屈服0.05mm/min 2 in span) | 13400 | psi | ASTM D 790 |
| 彎曲模量 (0.05mm/min 2 in span) | 339000 | psi | ASTM D 790 |
| 拉伸應(yīng)力 | ISO 527 | ||
| (屈服50mm/min) | 60 | MPa | |
| (斷裂 50mm/min) | 58 | MPa | |
| 拉伸應(yīng)變 | ISO 527 | ||
| (屈服50mm/min) | 5 | % | |
| (斷裂 50mm/min) | 90 | % | |
| 拉伸模量 (1mm/min) | 2330 | MPa | ISO 527 |
| 彎曲應(yīng)力 (屈服 2mm/min) | 93 | MPa | ISO 178 |
| 彎曲模量 (2mm/min) | 2210 | MPa | ISO 178 |
| 艾佐德沖擊 | ASTM D 256 | ||
| (缺口 73℉) | 12.5 | ft-lb/in | |
| (缺口-22℉) | 2 | ft-lb/in | |
| (缺口73℉ 0.250") | 2.9 | ft-lb/in | |
| 儀表控制抗沖擊總能量 | ASTM D 3763 | ||
| (73 ℉) | 540 | in-lb | |
| (-22℉) | 543 | in-lb | |
| 艾佐德沖擊 | ISO 180/1A | ||
| (缺口80*10*4 +23℃) | 59 | kJ/m2 | |
| (缺口80*10*4 -30℃) | 16 | kJ/m2 | |
| 簡支梁沖擊 (V缺口 Edgew80*10*4 sp=62mm) | 65 | kJ/m2 | ISO 179/1eA |
| 維卡軟化溫度 (速度 B/50) | 257 | ℉ | ASTM D 1525 |
| 熱變形溫度 | ASTM D 648 | ||
| (264英寸.0.125.未退火) | 199 | ℉ | |
| (66英寸.0.250.未退火) | 240 | ℉ | |
| (264英寸.0.250.未退火) | 225 | ℉ | |
| 熱膨脹系數(shù) | ASTM E 831 | ||
| (流動.-40℉ to 100℉) | 4.3E-05 | 1/℉ | |
| (x流動.-40℉ to 100℉) | 4.2E-05 | 1/℉ | |
| (流動.-40℉ to 200℉) | 4.6E-05 | 1/℉ | |
| (流動.-40℃ to40℃) | 7.75E-05 | 1/℃ | |
| (x流動.-40℃ to 40℃) | 7.57E-05 | 1/℃ | |
| 維卡軟化溫度 | ISO 306 | ||
| (速度 B/50) | 127 | ℃ | |
| (速度 B/120) | 130 | ℃ | |
| 熱變形溫度 Af (1.8MPa Flatw 80*10*4 sp=64mm) | 99 | ℃ | ISO 75/Af |
| 相對溫度指數(shù) (電氣) | 75 | ℃ | UL 746B |
| 機(jī)械相對溫度指數(shù)測試 | 75 | ℃ | UL 746B |
| 無機(jī)械相對溫度指數(shù)測試 | 75 | ℃ | UL 746B |
| 比重 | 1.22 | -- | ASTM D 792 |
| 比容 | 22.7 | in3/lb | ASTM D 792 |
| 成型收縮率 | SABIC Method | ||
| (流動0.125"(5)) | 0.5-0.7 | % | |
| (X流動0.125[(5)) | 0.6-0.8 | % | |
| 熔體流動速率 (250℃/5.0kgf) | 9.6 | g/10 min | ASTM D 1238 |
| 密度 | 0.04 | lb/in3 | ISO 1183 |
| 吸水率 | ISO 62 | ||
| (平衡.73℉) | 0.28 | % | |
| (23℃/50%RH) | 0.08 | % | |
| 熔體流動速率 (250℃/5.0kg) | 8 | g/10 min | ISO 1133 |
| 電弧電阻 PLC | 5 | PLC Code | ASTM D 495 |
| 電阻絲點火 PLC | 2 | PLC Code | UL 746A |
| 高壓電弧跟蹤速度 PLC | 2 | PLC Code | UL 746A |
| 高安培弧Ign,表面 PLC | 0 | PLC Code | UL 746A |
| 相比起痕指數(shù) UL PLC | 2 | PLC Code | UL 746A |
| 火焰等級 (公認(rèn)的.UL94) | 0.059 | in | UL94 |