| Grade : | ? ??X2CrNiMoN25-7-4耐腐蝕鋼片/板和帶材 | |||||||
| ? ??Number: | ? ? 1.4410 | |||||||
| ? ??Classification: | ? ? Austenitic-ferritic stainless steel - special grade | |||||||
| ? ??Density: | ? ? 7.8 ? g/cm 3 | |||||||
| ? ??Standard: | ? ? | |||||||
| EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件 | ||||||||
| EN 10088-3:2005不銹鋼。一般用途耐腐蝕鋼的半成品、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件 | ||||||||
| EN 10028-7:2007壓力用鋼制扁平產(chǎn)品。不銹鋼 | ||||||||
| EN 10222-5:2000壓力用鋼鍛件。馬氏體、奧氏體和奧氏體-鐵素體不銹鋼 | ||||||||
| EN 10216-5:2014壓力用無(wú)縫鋼管。技術(shù)交付條件。不銹鋼管 | ||||||||
| EN 10217-7:2005壓力用焊接鋼管。不銹鋼管 | ||||||||
| EN 10296-2:2005機(jī)械和一般工程用焊接圓鋼管。不銹鋼。技術(shù)交付條件 | ||||||||
| EN 10253-3:2008對(duì)焊管件。無(wú)特殊檢驗(yàn)要求的鍛造奧氏體和奧氏體-鐵素體（雙相）不銹鋼 | ||||||||
| EN 10253-4:2008對(duì)焊管件。有特殊檢驗(yàn)要求的鍛制奧氏體和奧氏體-鐵素體（雙相）不銹鋼 | ||||||||
| EN 10272:2007壓力用不銹鋼棒 | ||||||||
| EN 10250-4:2000一般工程用開(kāi)口鋼模鍛件。不銹鋼 | ||||||||
| EN 10297-2:2005機(jī)械和一般工程用無(wú)縫圓形鋼管。不銹鋼。技術(shù)交付條件 | ||||||||
| EN 10088-1:2005不銹鋼。不銹鋼清單 | ||||||||
| EN 10088-5:2009不銹鋼。建筑用耐腐蝕鋼棒材、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件 | ||||||||
| EN 10088-4:2009不銹鋼。建筑用耐腐蝕鋼片/板和帶材交貨技術(shù)條件 | ||||||||
| ? ??Equivalent grades: | ? ?? | |||||||
| Chemical comb % ? of ? steel ? X2CrNiMoN25-7-4 (1.4410): ? EN 10088-2-2005 | ||||||||
| 未經(jīng)買(mǎi)方同意，不得故意將本表中未列出的元素添加到鋼材中，除非對(duì)鑄件進(jìn)行精加工。 | ||||||||
| C | Si | Mn | Ni | P | S | Cr | Mo | N |
| max ? 0.03 | max ? 1 | max ? 2 | 6月8日 | max ? 0.035 | max ? 0.015 | 24 - 26 | 3 - 4.5 | 0.24 - 0.35 |
| Mechanical properties of ? steel ? X2CrNiMoN25-7-4 (1.4410)? | ||||||||
| Rm?- Tensile strength (MPa) (+A) | 730-1000 | |||||||
| Rm?- Tensile strength (MPa) (+AT) | 800-1000 | |||||||
| Rp0.2?0.2% proof strength (MPa) (+A) | 530-550 | |||||||
| Rp0.2?0.2% proof strength (MPa) (+AT) | 500-550 | |||||||
| KV?- Impact energy (J) transverse, (+A) | +20° | -40° | ||||||
| 90 | 40 | |||||||
| KV?- Impact energy (J) longitud., (+A) | +20° | |||||||
| 100-150 | ||||||||
| KV?- Impact energy (J) transverse, (+AT) | +20° | -40° | ||||||
| 100 | 40 | |||||||
| KV?- Impact energy (J) longitud., (+AT) | +20° | |||||||
| 100-200 | ||||||||
| A?- Min. elongation at fracture (%) (+A) | 15-25 | |||||||
| A?- Min. elongation at fracture (%) longitud., (+AT) | 20 | |||||||
| ? Brinell hardness ? (HB): ? (+A) | 290 | |||||||
| ? Brinell hardness ? (HB): ? (+AT) | 310? |