焊材特性
*焊后細化的碳化物均勻的分布在強化的基體內具有高抗磨性
*具有高抗磨性，產生奧氏體，堆焊材料中含初始碳化物
*工件表面堆焊后，再變形性有限
*材料不能機械加工處理
*應用溫度范圍不超過550℃
焊材應用
適用于對承受高度磨損和中等沖擊的部件作硬面處理，例如堆焊再制造電廠磨煤輥/盤瓦、水泥廠立磨磨輥/盤、礦山粉碎機輥、破碎機錘，制造耐磨復合鋼板，復合輥堆焊等。
參照標準：BS EN14700:2005
規(guī)格： Φ2.0mm、Φ2.4mm、Φ2.8mm、Φ3.2mm
包裝： 卷裝25 kg/卷、50kg/卷；桶裝200kg/桶
焊接指示： 不用加惰性氣體；交直流兩用；電弧要盡可能短
|
Bezeichnung |
Schlackentyp |
EN |
AWS |
|
MEGAFIL©710M |
Metal powder |
T 46 6 MM 1 H 5 |
E 70 C-6M H4 |
|
MEGAFIL©235M |
Metal powder |
T Mo1 M M 1 H5 |
E 80 C-D2-H4 |
|
MEGAFIL©236M |
Metal powder |
T CrMo1 M M 1 H5 |
E 80 C-B2 H4 |
|
MEGAFIL©240M |
Metal powder |
T 50 6 Ni M M 1H5 |
E 80 C-Ni1 H4 |
|
MEGAFIL©281M |
Metal powder |
T 46 4Z MM 1 H 5 |
E 80 C-G H4 |
|
MEGAFIL©741M |
Metal powder |
T 55 6 1NiMo B M 2 H5 |
E 90 C-K3M H4 |
|
MEGAFIL©940M |
Metal powder |
T 55 6 Mn1, 5Ni M M 1 H5 |
E 80 C-Ni2 H4 |
|
MEGAFIL©250M |
Metal powder |
T 69 6 Mn2, 5Ni M M 1 H5 |
E 80 C-Ni3 H4 |
|
MEGAFIL©742M |
Metal powder |
T 69 6 Mn2NiCrMo M M 1 H5 |
E 110 C-K4 H4 |
|
MEGAFIL©807M |
Metal powder |
T 89 0 Z M M 1 H5 |
E 120 C-K4 H4 |
|
MEGAFIL©1100M |
Metal powder |
T 89 4 Mn2NiCrMo M M 1 H5 |
E 120 C-K4 H4 |
|
MEGAFIL©713R |
rutile |
T 46 4(2) P M(C) 1 H5 |
E 71 T-1 M H4 |
|
MEGAFIL©781R |
rutile |
T 46 2 Z P M(C) 1 H5 |
E 81 T1-G H4 |
|
MEGAFIL©821R |
rutile |
T50(46)6(4)1Ni P M(C)1 H5 |
E 81 T1-Ni1 H4 |
|
MEGAFIL©822R |
rutile |
T46(50)4(6)1Ni P M(C)1 H5 |
E 81 T1-Ni1 H4 |
|
MEGAFIL©825R |
rutile |
T Mo P M1 H5 |
E 81 T1-A1M H4 |
|
MEGAFIL©836R |
rutile |
T CrMo 1 P M 1 H5 |
E 81 T1-B2 H4 |
|
MEGAFIL©731B |
rutile |
T 46 4 B M(C) 3 H5 |
E 70 T-5M H4 |
|
MEGAFIL©735B |
rutile |
T Mo B M3 H5 |
E 80 T5-A1M H4 |
|
MEGAFIL©736B |
rutile |
T CrMo1 B M 3 H5 |
E 80T5-B2 H4 |
|
MEGAFIL©737B |
rutile |
T CrMo2 B M 3 H5 |
E 80T5-B3 H4 |
|
MEGAFIL©838B |
rutile |
T CrMo1 B M 3 H5 |
E 80T5-B2 H4 |
|
MEGAFIL©741B |
rutile |
T 55 6 1NiMo B M(C) 3 H5 |
E 80 T5-K2M H4 |
|
MEGAFIL©742B |
rutile |
T 69 6 Mn2NiCrMo B M 3 H5 |
E 110 T5-K4M H4 |
|
MEGAFIL©745B |
rutile |
T 89 4 Mn2NiCrMo B M 3 H5 |
E 120 T5-K4M H4 |
|
MEGAFIL©807B |
rutile |
T 89 0 Z B M 3 H5 |
E 120 T5-K4M H4 |