材質(zhì) |
用途 |
化學(xué)成分 |
力學(xué)能力 |
線徑（mm） |
凈重(kg) |
閥芯直徑(mm) |
備注 |
|
ER304 |
主要用于焊接18Cr-8Ni鋼 |
C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% |
拉伸強度Mpa 1200 |
0.08-0.45 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER304L |
主要用于焊接17Cr-8Ni鋼 |
C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% |
拉伸強度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER308 |
主要用于焊接19Cr-9Ni鋼 |
C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% |
拉伸強度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER308L |
主要用于焊接20Cr-9Ni鋼 |
C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% |
拉伸強度Mpa 1200 |
0.8-4.5 |
5/12.5/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER309 |
主要用于焊接20Cr-13Ni鋼 |
C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10% |
拉伸強度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
材質(zhì) |
用途 |
化學(xué)成分 |
力學(xué)能力 |
線徑（mm） |
凈重(kg) |
閥芯直徑(mm) |
備注 |
|
ER304 |
主要用于焊接18Cr-8Ni鋼 |
C:0.064% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% |
拉伸強度Mpa 1200 |
0.08-0.45 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER304L |
主要用于焊接17Cr-8Ni鋼 |
C:0.028% Mn:1.65% Si:0.42% Ni:8.33% Cr:17.10% |
拉伸強度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER308 |
主要用于焊接19Cr-9Ni鋼 |
C:0.064% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% |
拉伸強度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER308L |
主要用于焊接20Cr-9Ni鋼 |
C:0.024% Mn:1.65% Si:0.42% Ni:10.33% Cr:20.10% |
拉伸強度Mpa 1200 |
0.8-4.5 |
5/12.5/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |
|
ER309 |
主要用于焊接20Cr-13Ni鋼 |
C:0.064% Mn:1.65% Si:0.42% Ni:14.33% Cr:20.10% |
拉伸強度Mpa 1200 |
0.08-4.5 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 TIG:1.0-4.5 |