| 詳細(xì)參數(shù) | |||
|---|---|---|---|
| 品牌/廠家 | Kepital | 類型 | 正牌料 |
| 用途級別 | 光學(xué)級 | 加工級別 | 注射 |
| 特性級別 | 耐高溫 | 外觀顏色 | 黑色 |
| 密度 | 1.35g/cm3 | 拉伸強(qiáng)度 | 23kg |
| 彎曲強(qiáng)度 | 53.0MPa | 缺口沖擊強(qiáng)度 | 140J/m |
| 斷裂伸長率 | 260% | 成型收縮率 | 87% |
| 熔體流動速率 | 7.0g/10min | ||
Kepital® TE-24
聚甲醛（POM）共聚物
Korea Engineering Plastics Co., Ltd
產(chǎn)品說明:
A medium viscosity grade improved on thermal stability, for general injection molding. It was modified with elastomer, and suitable for parts requiring a much higher impact resistance and toughness.
|
供貨地區(qū) |
|
|||||
|
特性 |
|
|||||
|
用途 |
|
|||||
|
RoHS 合規(guī)性 |
|
|||||
|
形式 |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|||
|
比重 |
|
|
|
|||
|
-- |
1.34 |
g/cm3 |
ASTM D792 |
|||
|
-- |
1.35 |
g/cm3 |
ISO 1183 |
|||
|
熔流率（熔體流動速率） |
|
|
|
|||
|
190°C/2.16 kg |
7.0 |
g/10 min |
ASTM D1238 |
|||
|
-- |
6.0 |
g/10 min |
ISO 1133 |
|||
|
收縮率 |
|
|
|
|||
|
流動 : 2.00 mm |
1.4 |
% |
ASTM D955 |
|||
|
3.00 mm |
1.7 |
% |
|
|||
|
吸水率 (平衡, 23°C, 60% RH) |
0.24 |
% |
ASTM D570 |
|||
|
機(jī)械性能 |
額定值 |
單位制 |
測試方法 |
|
抗張強(qiáng)度 |
|
|
|
|
屈服, 23°C |
39.0 |
MPa |
ASTM D638 |
|
屈服, 23°C |
41.0 |
MPa |
ISO 527-2 |
|
伸長率 (斷裂, 23°C) |
260 |
% |
ASTM D638 |
|
標(biāo)稱拉伸斷裂應(yīng)變 (23°C) |
> 60 |
% |
ISO 527-2 |
|
彎曲模量 |
|
|
|
|
23°C |
1540 |
MPa |
ASTM D790 |
|
23°C |
1450 |
MPa |
ISO 178 |
|
彎曲強(qiáng)度 |
|
|
|
|
23°C |
52.0 |
MPa |
ASTM D790 |
|
23°C |
53.0 |
MPa |
ISO 178 |
|
沖擊性能 |
額定值 |
單位制 |
測試方法 |
|
簡支梁缺口沖擊強(qiáng)度 |
18 |
kJ/m2 |
ISO 179/1eA |
|
懸壁梁缺口沖擊強(qiáng)度 (3.20 mm) |
140 |
J/m |
ASTM D256 |
|
|
|||