| 詳細(xì)參數(shù) | |||
|---|---|---|---|
| 品牌/廠家 | Hostaform | 類型 | 正牌料 |
| 用途級(jí)別 | 管材級(jí) | 加工級(jí)別 | 注射 |
| 特性級(jí)別 | 耐老化 | 外觀顏色 | 黑色 |
| 密度 | 1.59g/cm3 | 拉伸強(qiáng)度 | 23kg |
| 彎曲強(qiáng)度 | 59kg | 缺口沖擊強(qiáng)度 | 12kg.cm |
| 斷裂伸長(zhǎng)率 | 63% | 成型收縮率 | 87% |
| 熔體流動(dòng)速率 | 16.0cm3/10min | ||
Hostab® C 27021 GV3/30
聚甲醛（POM）共聚物
30% 玻璃珠
Celanese Corporation
產(chǎn)品說(shuō)明:
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 05-002, GB30
POM copolymer
With 30 % glass spheres reinforced, very easy flowing injection
molding type; low-warpage; high resistance to thermal and oxidative
degradation.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: low-warpage and dimensionally stable molded
parts with higher rigidity and hardness.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
|
填料/增強(qiáng)材料 |
|
|||||
|
特性 |
|
|||||
|
RoHS 合規(guī)性 |
|
|||||
|
加工方法 |
|
|||||
|
多點(diǎn)數(shù)據(jù) |
|
|||||
|
樹(shù)脂ID (ISO 1043) |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|||
|
密度 |
1.59 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
16.0 |
cm3/10min |
ISO 1133 |
|||
|
吸水率 (飽和, 23°C) |
0.90 |
% |
ISO 62 |
|||
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
拉伸模量 |
3800 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應(yīng)力 (屈服) |
38.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應(yīng)變 (屈服) |
6.0 |
% |
ISO 527-2/1A/50 |
|
標(biāo)稱拉伸斷裂應(yīng)變 |
12 |
% |
ISO 527-2/1A/50 |
|
拉伸蠕變模量 |
|
|
ISO 899-1 |
|
1 hr |
3300 |
MPa |
|
|
1000 hr |
2100 |
MPa |
|
|
彎曲模量 (23°C) |
3500 |
MPa |
ISO 178 |
|
|
|
|
|