| 詳細(xì)參數(shù) | |||
|---|---|---|---|
| 品牌/廠家 | Braskem | 類型 | 正牌料 |
| 用途級別 | 薄膜級 | 加工級別 | 擠出級 |
| 特性級別 | 耐低溫 | 外觀顏色 | 白色 |
| 密度 | 0.940g/cm3 | 拉伸強(qiáng)度 | 48kg |
| 彎曲強(qiáng)度 | 59kg | 缺口沖擊強(qiáng)度 | 25kg.cm |
| 斷裂伸長率 | 700% | 成型收縮率 | 87% |
| 熔體流動速率 | 0.70,g/10min | ||
Braskem EVA TN2006
乙烯醋酸乙烯共聚物
Braskem
產(chǎn)品說明:
TN2006 is an Ethylene-Vinyl Acetate (EVA) copolymer with good mechanical properties, high flexibility and toughness even with low temperature, excellent optical and salability properties. Additionally, this product has good water vapor barrier. The melt properties allow processability in tubular film equipment, being able to be coextruded in combination with many others materials
|
|
||||
|
總體 |
|
|||
|
材料狀態(tài) |
|
|||
|
添加劑 |
|
|||
|
特性 |
|
|||
|
用途 |
|
|||
|
機(jī)構(gòu)評級 |
|
|||
|
加工方法 |
|
|||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|
密度 |
0.940 |
g/cm3 |
ASTM D1505 |
|
熔流率（熔體流動速率） (190°C/2.16 kg) |
0.70 |
g/10 min |
ASTM D1238 |
|
醋酸乙烯含量 |
18.0 |
wt% |
|
|
硬度 |
額定值 |
單位制 |
測試方法 |
|
肖氏硬度 |
|
|
ASTM D2240 |
|
邵氏 A, 模壓成型 |
89 |
|
|
|
邵氏 D, 模壓成型 |
39 |
|
|
|
機(jī)械性能 |
額定值 |
單位制 |
測試方法 |
|
抗張強(qiáng)度 (斷裂, 模壓成型) |
4790 |
psi |
ASTM D638 |
|
伸長率 (斷裂, 模壓成型) |
680 |
% |
ASTM D638 |
|
薄膜 |
額定值 |
單位制 |
測試方法 |
|
薄膜厚度 - 經(jīng)測試 |
2.0 |
mil |
|
|
割線模量 |
|
|
ASTM D882 |
|
2% 正割, MD : 2.0 mil, 吹塑薄膜 |
5660 |
psi |
|
|
2% 正割, TD : 2.0 mil, 吹塑薄膜 |
5510 |
psi |
|
|
抗張強(qiáng)度 |
|
|
ASTM D882 |
|
MD : 斷裂, 2.0 mil, 吹塑薄膜 |
4640 |
psi |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
4500 |
psi |
|
|
伸長率 |
|
|
ASTM D882 |
|
MD : 斷裂, 2.0 mil, 吹塑薄膜 |
450 |
% |
|
|
TD : 斷裂, 2.0 mil, 吹塑薄膜 |
700 |
% |
|
|
落錘沖擊 (2.0 mil, 吹塑薄膜) |
600 |
g |
ASTM D1709B |
|
埃爾曼多夫抗撕強(qiáng)度 |
|
|
ASTM D1922 |
|
MD : 2.0 mil, 吹塑薄膜 |
150 |
g |
|
|
TD : 2.0 mil, 吹塑薄膜 |
|
|
|